UNTERSUCHUNGEN UEBER DIE OXIDATION UND DIE MECHANISCHEN EIGENSCHAFTEN VON ALUMINIUMGUSSEISEN BEI TEMPERATUREN VON 923 BIS 1373 K

Other title
INVESTIGATIONS INTO THE OXIDATION AND THE MECHANICAL PROPERTIES OF ALUMINUM CAST IRON AT TEMPERATURES FROM 923 TO 1373 K (en)
Author
PRZEWLOCKA H; SIEDLECKA J
Source
WERKST. KORROS.; DEU; DA. 1981-04; VOL. 32; NO 4; PP. 182-187; BIBL. 9 REF.
Document type
Article
Language
German
Keyword (fr)
ESSAI CORROSION CORROSION HAUTE TEMPERATURE OXYDATION AIR!SEC DURETE ESSAI CHOC RESISTANCE USURE RESISTANCE CORROSION PRODUIT CORROSION VITESSE CORROSION EFFET TEMPERATURE CALAMINE FONTE AL:0,5-1 MN:0,5-1 SI:0,1-0,5 C:1,9-2,8 P:0,01-0,05 S:0,01-0,05!SUB FONTE AL:3-5 MN:0,5-1 SI:0,1-0,5 C:1,9-2,8 P:0,05-0,1 S:0,01-0,05!SUB FONTE AL:5-10 MN:0,5-1 SI:0,1-0,5 C:1,9-2,8 P:0,01-0,05 S:0,01-0,05!SUB FONTE AL:5-10 MN:0,1-0,5 SI:1-1,5 C:2,8-4 P:0,1-0,5 S:0,01-0,05!SUB FONTE AL:15-20 MN:0,5-1 SI:3-5 C:0,9-1,9 P:0,05-0,1 S:0,01-0,05!SUB FONTE AL:20-30 MN:0,1-0,5 SI:1-1,5 C:0,9-1,9 P:0,05-0,1 S:0,01-0,05!SUB FONTE AL:20-30 MN:0,1-0,5 SI:2-2,5 C:0,9-1,9 P:0,01-0,05 S:0,01-0,05!SUB FONTE AL:20-30 MN:0,1-0,5 SI:1-1,5 C:0,9-1,9 P:0,01-0,05!SUB METALLURGIE
Keyword (en)
CORROSION TEST HIGH TEMPERATURE CORROSION OXIDATION AIR!SEC HARDNESS IMPACT TEST WEAR RESISTANCE CORROSION RESISTANCE CORROSION PRODUCT CORROSION RATE TEMPERATURE EFFECT OXIDE SCALE METALLURGY
Keyword (es)
METALURGIA
Classification
Pascal
001 Exact sciences and technology / 001D Applied sciences / 001D11 Metals. Metallurgy

Discipline
Metals. Metallurgy
Origin
Inist-CNRS
Database
PASCAL
INIST identifier
PASCAL8300172594

Sauf mention contraire ci-dessus, le contenu de cette notice bibliographique peut être utilisé dans le cadre d’une licence CC BY 4.0 Inist-CNRS / Unless otherwise stated above, the content of this bibliographic record may be used under a CC BY 4.0 licence by Inist-CNRS / A menos que se haya señalado antes, el contenido de este registro bibliográfico puede ser utilizado al amparo de una licencia CC BY 4.0 Inist-CNRS

Searching the Web